TECHNYL eXten® D 218CR V33 Black is a glass fiber reinforced grade based on polyamide blend of polyamide 6.10 and polyamide 66, heat stabilized, for injection moulding. This grade shows outstanding resistance to hydrolysis and chemical resistance to long life automotive coolants. It also offers an excellent crack resistance to calcium chloride road salts, good injection process ability, high surface aspect quality, and high overall mechanical and thermal properties.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedGood Heat AgingGood SurfaceRenewable ResourceChemical ResistanceHydrolysis ResistanceChlorid(CaCl2/Salt)ResitanceGlycol resistanceLow Moisture AbsorptionFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Compliance | REACH (EC 1907/2006)RoHS | |||
| Reinforced | 33% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
Across Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond., 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Dry |
Break | *** Mpa | ISO 527-1/-2 | cond. |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Dry |
Break | *** % | ISO 527-1/-2 | cond. |
Flexural Modulus | *** Mpa | ISO 178 | Dry. 2 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | cond., 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry. 2 mm/min |
- | *** Mpa | ISO 178 | cond. |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | cond. |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1 | 10°C/min |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.