30% glass fiber reinforced, for injection molding, grey
TECHNYL® ONE J 60X1 V30 grey 2682 LP is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber with best-in-class fire protection behavior, for injection moulding. A full yellow card is available with a UL94 V0 rating at 0.4 mm, unmatched thermal ageing properties (150°C electrical RTI - Relative Thermal Index), and outstanding electrical properties, including a high comparative tracking index (CTI 0 for 600 volts and higher). This product has superior electrical performance compared to traditional high-performance plastics.
Its low corrosion ensures processing tools longevity.
This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热耐热老化阻燃无卤耐腐蚀高流动填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状灰色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1.1 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 0.63 % | ISO 62 | 24 hr, 23°C |
吸湿率 | 1.4 % | ISO 62 | T=23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 150 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 2.7 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 230 Mpa | ISO 178 | Dry. 2 mm/min |
- | 190 Mpa | ISO 178 | cond., 2 mm/min |
弯曲模量 | 9000 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 8000 Mpa | ISO 178 | cond., 2 mm/min |
拉伸模量 | 11000 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 58 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 9 kJ/m² | ISO 180/1A | Dry |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 50 kJ/m² | ISO 180/1U | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 274 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 250 °C | ISO 75 | |
熔融温度(Tm) | 270 °C | ISO 11357-1 | 10°C/min |
加工温度 | 285~300 °C | - | |
模具温度 | 90~110 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。