Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard). For specific content see sustainability declaration.
(PC+PET) blend, easy flow, impact modified; application: automotive body panels
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Toughened/Impact ModifiedGood Flow | |||
| Additive | Impact Modifier | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
270°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 2577 | 150x105x3 mm; 270 °C / MT 70°C; 600 bar |
Across Flow | ***~*** % | ISO 2577 | 150x105x3 mm; 270 °C / MT 70°C; 600 bar |
Viscosity | *** Pa-s | ISO 11443 | 1000 s-1; 270 °C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
3.5% strain | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strain | |||
- | *** % | ISO 178 | 2 mm/min |
Puncture | |||
Force | *** N | ISO 6603-2 | -30°C |
Force | *** N | ISO 6603-2 | 23°C |
Energy | *** J | ISO 6603-2 | -30°C |
Energy | *** J | ISO 6603-2 | 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180 | |
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120 °C/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.