Additive manufacturing thermoplastiv polyurethane grade for powder bed fusion such as Selective Laser Sintering (SLS) and High Speed Sintering (HSS).
Ether-type; tough and rigid; very good hydrolysis and microbial resistance; very good low-temperature impact strength; UV resistant.
| Original Document | Technical Datasheet(English) | |||
| Features | High Impact at Low TemperaturGood FlexibilityAntimicrobialUV StabiltiyHydrolysis Resistance | |||
| Appearance | PowderWhite | |||
| Processing | Selective Laser Sintering(SLS)3D Printing | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | powder bed |
Density/Specific Gravity | *** g/cm³ | Internal | printed bar |
Particle Size | *** micrometer | Internal | X10 |
Particle Size | *** micrometer | Internal | X50 |
Particle Size | *** micrometer | Internal | X90 |
Bulk(Apparent ) Density | *** g/cm³ | Internal | powder |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | xy-direction, 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | xy-direction, 1 mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527-2 | xy-direction, 200 mm/min |
- | *** Mpa | ISO 527-2 | z-direction, 200 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | xy-direction, 200 mm/min |
Break | *** % | ISO 527-2 | z-direction, 200 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | xy-direction |
Flexural Modulus | *** Mpa | ISO 178 | xy-direction |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
- | *** kJ/m² | ISO 179 | z-direction |
Charpy Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 179 | xy-direction |
Izod Notched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | z-direction |
Izod Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | xy-direction |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 7619-1 | 1s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10 N; 120 °C/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N ; 50 °C/h |
Glass Transition Temperature | ***~*** °C | Internal | DMA (1 Hz; 2 °C/min) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.