Formerly Makrolon KU1-1205; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; flame retardant; high viscosity; extrusion; solid sheet; aircraft construction; automotive construction; railway construction
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Flame RetardantHigh Viscosity | |||
| Processing | ExtrusionSheet Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 2577 | |
Across Flow | ***~*** % | ISO 2577 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Puncture | |||
Force | *** N | ISO 6603-2 | -30℃, maximum force |
Force | *** N | ISO 6603-2 | 23℃, maximum force |
Energy | *** J | ISO 6603-2 | -30℃ |
Energy | *** J | ISO 6603-2 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
-60℃ (-76℉) | *** kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 180/A | 3 mm,partial break |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50°C/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Processing Temperature | *** °C | - | |
Mould temperature | *** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Glow Wire Flammability Index(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Vertical Burn | *** sec | FAR 25.853 | 1.0 mm, passed |
Vertical Burn | *** sec | FAR 25.853 | 1.0 mm, passed |
Vertical Burn | *** sec | FAR 25.853 | 1.5 mm, passed |
Vertical Burn | *** sec | FAR 25.853 | 1.5 mm, passed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.