MVR (300 °C/1.2 kg) 16 cm³/10 min; low viscosity; easy release; flame retardant; impact modified; injection molding - melt temperature 300°C; electrical/electronic; housing parts
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Toughened/Impact ModifiedFlame RetardantMold ReleaseLow viscosity | |||
| Additive | Flame RetardantImpact Modifier | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 2577 | |
Across Flow | ***~*** % | ISO 2577 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
Puncture | |||
Force | *** N | ISO 6603-2 | 23℃, maximum force |
Energy | *** J | ISO 6603-2 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | complete break |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | partial break |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | 3 mm,complete break |
23℃ (73℉) | *** kJ/m² | ISO 180/A | 3 mm,partial break |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 120 °C/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N; 50 °C/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
Processing Temperature | *** °C | - | |
Mould temperature | *** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.