POKETONE Polymer M33AF2Y is a flame-retarded high-flow injection moulding grade with mechanical properties which classify it as an engineerring thermoplastic. This grade offers UL94 V-0 rating, high comparative tracking and glow-wire indices, all without the use of halogenated or red phosphorus flame retardants. The benign flame-retardant system used for POKETONE Polymer M33AF2Y ensures that the smoke density and toxicity are both low. Yet this grade retains the exceptional blend of properties of the base polymer, such as low moisture absorption, good toughness and high resistance to a wide range of chemicals.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤无红磷低挥发VOC高流动 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | *** g/cm³ | ASTM D792 | |
比重 | *** g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
240℃/2.16kg | *** g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | *** % | ASTM D 955 | 3mm |
横向(Across Flow) | *** % | ASTM D 955 | 3mm |
吸水率 | *** % | ASTM D570 | |
吸水率 | *** % | ISO 62 | |
吸湿率 | *** % | ISO 62 | |
吸湿率 | *** % | ASTM D 570 | |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** Mpa | ASTM D638 | |
拉伸模量 | *** Mpa | ISO 527-1 | |
拉伸强度 | |||
屈服(yld) | *** Mpa | ASTM D638 | |
屈服(yld) | *** Mpa | ISO 527-1 | |
拉伸延伸率 | |||
断裂(brk) | *** % | ASTM D638 | |
断裂(brk) | *** % | ISO 527-1 | |
弯曲模量 | *** Mpa | ASTM D790 | |
弯曲模量 | *** Mpa | ISO 178 | |
弯曲强度 | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
维卡软化温度(Vicat) | *** °C | ASTM D1525 | |
维卡软化温度(Vicat) | *** °C | ISO 306 | |
熔融温度(Tm) | *** °C | ASTM D3418 | |
熔融温度(Tm) | *** °C | ISO 11357 | |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
防火等级 | |||
V-0 | *** mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
2.0mm | *** °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
体积电阻率 | *** Ohm-cm | ASTM D257 | |
表面电阻率 | *** Ohm | ASTM D257 | |
介电常数(DK) | |||
60 Hz | *** - | ASTM D 150 | |
耗散因数(DF) | |||
60 Hz | *** E-4 | ASTM D 150 | |
相对漏电起痕指数(CTI ) | |||
- | PLC | UL 746A | 3mm |
绝缘强度 | *** kV/mm | ASTM D149 | |
绝缘强度 | *** kV/mm | ASTM D149 | |
高电压电弧起痕速率(HVTR) | *** PLC | UL 746A | 3mm |
热线圈起燃性(HWI) | *** PLC | UL 746A | |
高电流电弧起燃性(HAI) | PLC | UL 746A |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。