POKETONE Polymer M630A is a general-purpose injection moulding grade with mechanical properties which classify it as an engineering thermoplastic. This grade has an excellent balance of stiffness and toughness over a broad temperature range, high resilience and good wear resistance.This grade exhibits very good processability, good impact resistance, high resilience and good creep performance. POKETONE Polymer M630A can also withstand short-term exposure to elevated temperatures. Moreover this polymer exhibits a high resistance to hydrocarbons, solvents, salt solutions, weak acids and weak bases.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.24 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | 5.6 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
240℃/2.16kg | 6 g/10 min | ASTM D 1238 | |
240℃/2.16kg | 1.24 g/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.6 % | ASTM D 955 | 2mm |
纵向(Flow) | 2.1 % | ASTM D 955 | 3mm |
横向(Across Flow) | 1.5 % | ASTM D 955 | 2mm |
横向(Across Flow) | 2.1 % | ASTM D 955 | 3mm |
吸水率 | 2.1 % | ASTM D570 | |
吸水率 | 2.1 % | ISO 62 | |
吸湿率 | 0.5 % | ISO 62 | |
吸湿率 | 0.5 % | ASTM D 570 | |
磨耗 | 12 mg/1000cy | ASTM D 1044 | 1 kg load, CS-17 wheel |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | |
屈服(yld) | 58 Mpa | ISO 527-1 | |
拉伸延伸率 | |||
屈服(yld) | 22 % | ASTM D638 | |
屈服(yld) | 22 % | ISO 527-1 | |
断裂(brk) | 300 % | ASTM D638 | |
断裂(brk) | 300 % | ISO 527-1 | |
弯曲强度 | |||
- | 53 Mpa | ASTM D790 | |
- | 53 Mpa | ISO 178 | |
弯曲模量 | 1350 Mpa | ASTM D790 | |
弯曲模量 | 1250 Mpa | ISO 178 | |
拉伸模量 | 1450 Mpa | ASTM D638 | |
拉伸模量 | 1350 Mpa | ISO 527-1 | |
摩擦系数 | 0.36 - | Internal | Friction against steel,1.3 MPa 0.06 m/sec |
摩擦系数 | 0.15 - | Internal | Friction agatinst self,1.3 MPa 0.06 m/sec |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3 kJ/m² | ISO 179/1eA | |
-10℃ (14℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 17 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 52 J/m | ASTM D256 | |
-30℃ (-22℉) | 4 kJ/m² | ISO 180/A | |
-10℃ (14℉) | 65 J/m | ASTM D256 | |
-10℃ (14℉) | 6 kJ/m² | ISO 180/A | |
23℃ (73℉) | 220 J/m | ASTM D256 | |
23℃ (73℉) | 15 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | |
多轴冲击 | 50 J | ISO 6603 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 110 R | ASTM D785 | |
邵氏硬度 D | 73 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 195 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 185 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 102 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ISO 75 | |
维卡软化温度(Vicat) | 192 °C | ASTM D1525 | 5 kg |
维卡软化温度(Vicat) | 190 °C | ISO 306 | |
线性膨胀系数(CLTE) | |||
- | 100 E-6/°C | ASTM D E831 | 25℃ to 55℃ |
熔融温度(Tm) | 222 °C | ASTM D3418 | |
熔融温度(Tm) | 222 °C | ISO 11357 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+17 Ohm | ASTM D257 | |
介电常数(DK) | |||
60 Hz | 6.1 - | ASTM D 150 | |
耗散因数(DF) | |||
60 Hz | 90 E-4 | ASTM D 150 | |
绝缘强度 | 19 kV/mm | ASTM D149 | 2mm |
绝缘强度 | 15 kV/mm | ASTM D149 | 3mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。