High strength, hydrolytic stability, low warpage, low specific gravity, and dimensional stability. NORYL PX5534 is an excellent candidate for central heating parts, water filters, and water meter components.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHeat StabilizedFlame RetardantHalogen FreeCl- FreeBr- FreeDimensional StabilityLow WarpageLow ShrinkageHydrolysis ResistanceLow DensityLow Moisture Absorption | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | |
Across Flow | ***~*** % | Internal | |
Water Absorption | *** % | ASTM D570 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Instrumented Impact Energy | |||
23℃ (73℉)peak | *** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | Min. |
V-0 | *** mm | UL94 | Min. |
5VA | *** mm | UL94 | Min. |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | ASTM D150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI)-PLC | |||
PLC2 (250 - 399 V) | *** - | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in air, 3.2 mm |
Arc Resistance-PLC | |||
PLC6 (60 -119 s) | *** - | ASTM D495 | |
High Voltage Arc Tracking Rate(HVTR)-PLC | |||
PLC3 (80.1-150 mm/min) | *** - | UL 746A | |
Hot Wire Ignition(HWI)-PLC | |||
PLC0 (≥ 120 s) | ≥ *** mm | UL 746A | |
High Ampere Arc Ignition(HAI)-PLC | |||
PLC0 (≥ 120 times) | ≥ *** mm | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.