NORYL PX1630 is a 30% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS).
| Original Document | Technical Datasheet(English) | |||
| Solutions | HV Distribution/Switching Unit for EV Battery Packs | |||
| Features | Dimensional StabilityLow WarpageLow ShrinkageDrinking Water ContactHydrolysis ResistanceLow DensityLow Moisture AbsorptionFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
300°C/10.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Across Flow | ***~*** % | Internal | flow, 3.2 mm |
Water Absorption | *** % | ISO 62-1 | 23°C/saturated |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
Abrasion resistance | *** mg/1000cy | Internal | Taber Abrasion, CS-17, 1 kg |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Break | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
Multiaxial Impact | *** J | ISO 6603 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | H358/30 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate A/50 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/120 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
Ball Pressure Test | *** °C | IEC 60695-10-2 | PASS |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Min. |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | ROA |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | in oil, 3.2 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.