NORYL N190 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, nonchlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F1. NORYL N190 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for a variety of applications such as solar frames, unattended power supply (UPS) inverter/charger, indoor and outdoor electrical enclosures / housings / connectors, and wall plates / sockets / switches. *This grade is also referred to as NORYL N1900 in several regions.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击阻燃无卤无氯无溴尺寸稳定低翘曲低收缩耐候性耐水解低密度低吸湿性 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.1 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
280°C/2.16 kg | 8 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | on Tensile Bar, flow |
吸水率 | 0.32 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.06 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 40 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3 % | ISO 527 | 50 mm/min |
断裂(brk) | 20 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 75 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2200 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2300 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 87 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 90 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 80 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 110 °C | ISO 306 | Rate A/50 |
维卡软化温度(Vicat) | 105 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 95 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 80 °C | UL 746B | |
电气Elec,- | 95 °C | UL 746B | |
强度Str,- | 95 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 90 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
导热系数 | 0.25 W/m-°C | ISO 8302 | |
球压痕温度 | 75 °C | IEC 60695-10-2 | PASS |
球压痕温度 | 95 °C | IEC 60695-10-2 | approximate maximum |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | Min. |
5VA | 3 mm | UL94 | Min. |
氧指数(LOI) | 30 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
3.2mm | 960 °C | IEC 60695-2-12 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | ROA |
介电常数(DK) | |||
50/60 Hz | 2.7 - | IEC 60250 | |
1MHz | 2.6 - | IEC 60250 | |
耗散因数(DF) | |||
50/60 Hz | 4 E-4 | IEC 60250 | |
1MHz | 9 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
- | 1 PLC | IEC 60112 | |
- | 250 V | IEC 60112 | |
耐电弧性 | 6 PLC | UL 746A | Tungsten |
高电压电弧起痕速率(HVTR) | 4 PLC | UL 746A | |
热线圈起燃性(HWI) | 1 PLC | UL 746A | ≥1.5mm |
高电流电弧起燃性(HAI) | 1 PLC | UL 746A | ≥1.5mm |