LIMITED USE, No New Customers / Applications as of Jan. 2010:
PBT+PC alloy with impact modifier and FR package for electrical markets. Extrusion Grade, Flame retardant, Impact Modified, Mold Release, Opaque, UL Grade,
| Original Document | Technical Datasheet(English) | |||
| Features | Toughened/Impact ModifiedFlame RetardantMold Release | |||
| Additive | Flame RetardantImpact ModifierRelease Agent | |||
| Appearance | Opaque Color | |||
| Processing | Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 0.75-2.3 mm |
Flow | ***~*** % | Internal | flow, 2.3-4.6 mm |
Across Flow | ***~*** % | Internal | xflow, 0.75-2.3 mm |
Across Flow | ***~*** % | Internal | xflow, 2.3-4.6 mm |
Outdoor Suitability UL F1/F2 | |||
F2 | *** - | UL 746C | |
Water Absorption | *** % | ASTM D570 | 23°C/24hrs |
Specific Volume | *** cm³/g | ASTM D792 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Falling Dart Impact | *** J | ASTM D 3029 | Gardner, 23°C |
Falling Dart Impact | *** J | ASTM D 3029 | Modified Gardner, 23°C |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Flow | *** E-6/°C | ASTM E831 | 60°C to 138°C, flow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | ASTM D 150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
100Hz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in air, 3.2 mm |
Dielectric Strength | *** kV/mm | ASTM D149 | in oil, 1.6 mm |
Dielectric Strength | *** kV/mm | ASTM D149 | in oil, 3.2 mm |
Arc Resistance | *** PLC | ASTM D495 | Tungsten |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.