Viton™ B-601C* is an incorporated cure “B-family” polymer that demonstrates improved processing properties when compared to older “B-family” terpolymer fluoroelastomers. The improved properties provide excellent compound flow in molding (compressions, injection, transfer) parts, where the heat and fluid characteristics of a “B-family” Viton™ are needed.
Compared with older “B-family” terpolymers, Viton™ B-601C provides:
• Fully precompounded
– O-ring curative level
• Improved processing
– Better mixing
– Excellent scorch safety
– Better mold release with less mold fouling
• Medium to fast cure rate
• Improved compression set
Applications
O-rings, gaskets, and other molded parts requiring properties of a terpolymer “B-family” Viton™.
| Original Document | Technical Datasheet(English) | |||
| Appearance | SlabWhite | |||
| Processing | InjectionCompression MouldingResin Transfer Molding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | |
Mooney Viscosity | *** MU | Internal | ML 1+10, 121°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 412 | 23 °C, After Aging 168 hr at 200 °C |
- | *** Mpa | ASTM D 412 | 23 °C, After Aging 70 hr at 200 °C |
- | *** Mpa | ASTM D 412 | 23 °C, After Aging 70 hr at 232 °C |
- | *** Mpa | ASTM D 412 | 23 °C, Original, No post-cure |
- | *** Mpa | ASTM D 412 | 23 °C, Original, Post-cured |
at 100% strain | *** Mpa | ASTM D 412 | 23 °C, After Aging 168 hr at 200 °C |
at 100% strain | *** Mpa | ASTM D 412 | 23 °C, After Aging 70 hr at 200 °C |
at 100% strain | *** Mpa | ASTM D 412 | 23 °C, After Aging 70 hr at 232 °C |
at 100% strain | *** Mpa | ASTM D 412 | 23 °C, Original, No post-cure |
at 100% strain | *** Mpa | ASTM D 412 | 23 °C, Original, Post-cured |
Tensile Elongation | |||
Break | *** % | ASTM D 412 | 23 °C, After Aging 168 hr at 200 °C |
Break | *** % | ASTM D 412 | 23 °C, After Aging 70 hr at 200 °C |
Break | *** % | ASTM D 412 | 23 °C, After Aging 70 hr at 232 °C |
Break | *** % | ASTM D 412 | 23 °C, Original, No post-cure |
Break | *** % | ASTM D 412 | 23 °C, Original, Post-cured |
Compression Set | *** % | ASTM D 395 | 70 hr at 200 °C, Method B, O-Rings |
Compression Set | *** % | ASTM D 395 | 70 hr at 23 °C, Method B, O-Rings |
Compression Set | *** % | ASTM D 395 | 70 hr at 232 °C, Method B, O-Rings |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ASTM D 2240 | 23 °C, After Aging 168 hr at 200 °C |
Shore A hardness | *** A | ASTM D 2240 | 23 °C, After Aging 70 hr at 200 °C |
Shore A hardness | *** A | ASTM D 2240 | 23 °C, After Aging 70 hr at 232 °C |
Shore A hardness | *** A | ASTM D 2240 | 23 °C, Original, No post-cure |
Shore A hardness | *** A | ASTM D 2240 | 23 °C, Original, Post-cured |
| Aging | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Change in Volume | *** % | ASTM D471 | Fuel C, 168 hr at 23 °C |
Change in Volume | *** % | ASTM D471 | Methanol, 168 hr at 23 °C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.