| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| Internal | |
门尼粘度 |
*** MU
| ASTM 1646 | |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
*** Mpa | ASTM D 412 | 23 °C, Original, no post-cure |
断裂(brk) |
*** Mpa | ASTM D 412 | 23 °C, Original, post-cure |
100%延伸率时 |
*** Mpa | ASTM D 412 | 23 °C, Original, no post-cure |
100%延伸率时 |
*** Mpa | ASTM D 412 | 23 °C, Original, post-cure |
拉伸延伸率 | | | |
断裂(brk) |
*** % | ASTM D 412 | 23 °C, Original, no post-cure |
断裂(brk) |
*** % | ASTM D 412 | 23 °C, Original, post-cure |
压缩永久形变 |
*** %
| ASTM D 395 | 168 hr at 200 °C, Method B plied disks |
压缩永久形变 |
*** %
| ASTM D 395 | 70 hr at 150 °C, Method B plied disks |
压缩永久形变 |
*** %
| ASTM D 395 | 70 hr at 200 °C, Method B plied disks |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
邵氏硬度 A |
*** A
| ASTM D 2240 | 23 °C, Original, no post-cure |
邵氏硬度 A |
*** A
| ASTM D 2240 | 23 °C, Original, post-cure |
| 老化性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
硬度 (热老化) |
*** -
| ASTM D2240 | 23 °C, After aging 168 hr at 200 °C |
硬度 (热老化) |
*** -
| ASTM D2240 | 23 °C, After aging 168 hr at 250 °C |
硬度 (热老化) |
*** -
| ASTM D2240 | Change, After aging 168 hr at 200 °C |
硬度 (热老化) |
*** -
| ASTM D2240 | Change, After aging 168 hr at 250 °C |
拉伸强度(热老化) |
*** Mpa
| ASTM D 412 | 23 °C, After aging 168 hr at 200 °C |
拉伸强度(热老化) |
*** Mpa
| ASTM D 412 | 23 °C, After aging 168 hr at 250 °C |
拉伸强度(热老化) |
*** Mpa
| ASTM D 412 | 23 °C, M100, After aging 168 hr at 250 °C |
拉伸强度(热老化) |
*** Mpa
| ASTM D 412 | 23 °C,M100, After aging 168 hr at 200 °C |
拉伸强度(热老化) |
*** %
| ASTM D 412 | Change M100, After aging 168 hr at 200 °C |
拉伸强度(热老化) |
*** %
| ASTM D 412 | Change M100, After aging 168 hr at 250 °C |
拉伸强度(热老化) |
*** %
| ASTM D 412 | Change, After aging 168 hr at 200 °C |
拉伸强度(热老化) |
*** %
| ASTM D 412 | Change, After aging 168 hr at 250 °C |
延伸率(热老化) |
*** %
| ASTM D 412 | 23 °C, After aging 168 hr at 200 °C |
延伸率(热老化) |
*** %
| ASTM D 412 | 23 °C, After aging 168 hr at 250 °C |
延伸率(热老化) |
*** %
| ASTM D 412 | Change, After aging 168 hr at 200 °C |
延伸率(热老化) |
*** %
| ASTM D 412 | Change, After aging 168 hr at 250 °C |
体积变化 |
*** %
| ASTM D471 | ASTM 105 Oil, 70 hr at 150 °C |
体积变化 |
*** %
| ASTM D471 | Fuel C, 70 hr at 23 °C |
体积变化 |
*** %
| ASTM D471 | Methanol, 70 hr at 23 °C |
体积变化 |
*** %
| ASTM D471 | Stauffer 7700 Fluid, 70 hr at 200 °C |