Viton™ A-401C

FKM

科慕化学(Chemours)

产品描述
基本信息
原厂资料
物性表(英文)
颜色形状
板材
白色
成型方式
挤出
模压
技术参数
物理性能 值/单位(登录后可见) 测试标准 测试条件

密度/比重

 *** g/cm³ Internal

门尼粘度

 *** MU Internal
ML 1+10, 121°C
机械性能 值/单位(登录后可见) 测试标准 测试条件

拉伸强度

-

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 200 °C

-

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C

-

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 232 °C

-

*** Mpa ASTM D 412
23 °C, Original, No post-cure

-

*** Mpa ASTM D 412
23 °C, Original, post-cured

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 200 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 232 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, Original, No post-cure

100%延伸率时

*** Mpa ASTM D 412
23 °C, Original, post-cured

拉伸延伸率

断裂(brk)

*** % ASTM D 412
23 °C, After aging 168 hr at 200 °C

断裂(brk)

*** % ASTM D 412
23 °C, After aging 70 hr at 200 °C

断裂(brk)

*** % ASTM D 412
23 °C, After aging 70 hr at 232 °C

断裂(brk)

*** % ASTM D 412
23 °C, Original, No post-cure

断裂(brk)

*** % ASTM D 412
23 °C, Original, post-cured

压缩永久形变

 *** % ASTM D 395
168 hr at 200 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
336 hr at 200 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
70 hr at 200 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
70 hr at 23 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
70 hr at 232 °C, Method B, O-Rings
硬度性能 值/单位(登录后可见) 测试标准 测试条件

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 168 hr at 200 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 70 hr at 200 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 70 hr at 232 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, Original, No post-cure

邵氏硬度 A

 *** A ASTM D 2240
23 °C, Original, post-cured

此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。