Viton™ A-700

FKM

科慕化学(Chemours)

产品描述
基本信息
原厂资料
物性表(英文)
颜色形状
粒状
灰色
褐色
成型方式
挤出
模压
涂装
共混改性
技术参数
物理性能 值/单位(登录后可见) 测试标准 测试条件

密度/比重

 *** g/cm³ Internal

门尼粘度

 *** MU Internal
ML 1+10, 121°C
机械性能 值/单位(登录后可见) 测试标准 测试条件

拉伸强度

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 200 °C

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 23 °C (73 °F) in 85% Reg. Fuel °C/15% Methanol

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 250 °C

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C (392 °F) in IRM-902 Oil

断裂(brk)

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 250 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 200 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 23 °C (73 °F) in 85% Reg. Fuel °C/15% Methanol

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 168 hr at 250 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 200 °C (392 °F) in IRM-902 Oil

100%延伸率时

*** Mpa ASTM D 412
23 °C, After aging 70 hr at 250 °C

拉伸延伸率

断裂(brk)

*** % ASTM D 412
23 °C, After aging 168 hr at 200 °C

断裂(brk)

*** % ASTM D 412
23 °C, After aging 168 hr at 23 °C (73 °F) in 85% Reg. Fuel °C/15% Methanol

断裂(brk)

*** % ASTM D 412
23 °C, After aging 168 hr at 250 °C

断裂(brk)

*** % ASTM D 412
23 °C, After aging 70 hr at 200 °C

断裂(brk)

*** % ASTM D 412
23 °C, After aging 70 hr at 200 °C (392 °F) in IRM-902 Oil

断裂(brk)

*** % ASTM D 412
23 °C, After aging 70 hr at 250 °C

压缩永久形变

 *** % ASTM D 395
168 hr at 200 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
22 hr at 232 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
70 hr at 150 °C, Method B, O-Rings

压缩永久形变

 *** % ASTM D 395
70 hr at 200 °C, Method B, O-Rings
硬度性能 值/单位(登录后可见) 测试标准 测试条件

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 168 hr at 200 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 168 hr at 23 °C (73 °F) in 85% Reg. Fuel °C/15% Methanol

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 168 hr at 250 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 70 hr at 200 °C

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 70 hr at 200 °C (392 °F) in IRM-902 Oil

邵氏硬度 A

 *** A ASTM D 2240
23 °C, After aging 70 hr at 250 °C
热学性能 值/单位(登录后可见) 测试标准 测试条件

低温回缩(TR)

 *** °C ASTM D1329
TR-10
老化性能 值/单位(登录后可见) 测试标准 测试条件

体积变化

 *** % ASTM D471
23 °C, After aging 168 hr at 23 °C (73 °F) in 85% Reg. Fuel °C/15% Methanol

体积变化

 *** % ASTM D471
23 °C, After aging 70 hr at 200 °C (392 °F) in IRM-902 Oil

此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。