Heat stabilized, partially aromatic polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures and excellent chemical resistance for highly stressed parts. The product can be characterized as compound with high strength and stiffness, very low water absorption and outstanding dimensional stability. It features a high melting point (320°C) and excellent melt stability.
Markets & applications
Automotive: Fuel system, cooling system, powertrain, thermostat housing, pumps, fuel cell
E&E: Sensors, SMT applications (surface mount technology)
Industry goods: Pumps, compressors
Consumer goods: home appliances, consumer electronics, furniture fittings
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceHeat StabilizedDimensional StabilityChemical ResistanceLow Moisture AbsorptionFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | 24 h in water, 23 °C |
Water Absorption | *** % | ISO 62 | saturation in water at 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h. |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | 0.5% in 96 % H2SO4 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 120°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 170°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 80°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond., 23°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond., 80°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | 120°C |
Break | *** Mpa | ISO 527-1/-2 | 170°C |
Break | *** Mpa | ISO 527-1/-2 | 23°C |
Break | *** Mpa | ISO 527-1/-2 | 80°C |
Break | *** Mpa | ISO 527-1/-2 | cond., 23°C |
Break | *** Mpa | ISO 527-1/-2 | cond., 80°C |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | 120°C |
Break | *** % | ISO 527-1/-2 | 170°C |
Break | *** % | ISO 527-1/-2 | 23°C |
Break | *** % | ISO 527-1/-2 | 80°C |
Break | *** % | ISO 527-1/-2 | cond., 23°C |
Break | *** % | ISO 527-1/-2 | cond., 80°C |
Flexural Modulus | *** Mpa | ISO 178 | 23°C |
Flexural Modulus | *** Mpa | ISO 178 | cond., 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
- | *** Mpa | ISO 178 | cond. |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Above |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23-55 °C |
Across Flow | ***~*** E-6/K | ISO 11359-1/-2 | 23-55 °C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | 150°C |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | cond. |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | cond. |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | K20/K20, ( 60*60*1 mm³) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.