Applications:
-Low temperature (-40 ℃) impact resistance , Mobile equipment housing, Connectors, Switches, Outdoor equipment component, Battery pack.
Features:
-Translucent,Mid flow,Flame retardant,Low temperature impact property,UV resistance.
| Original Document | Technical Datasheet-ASTM(Chinese&English) Technical Datasheet-ASTM(English) | |||
| Features | High Impact at Low TemperaturFlame RetardantUV StabiltiyMedium viscosity | |||
| Appearance | Pellets/GranulesTranslucent | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23℃ |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | 3.2mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | 23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | 23℃ |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 23℃ |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Unnotched Impact Strengh | |||
-40℃ (-40℉) | *** kg·cm/cm | ASTM D256 | 1/8" bar |
-30℃ (-22℉) | *** kg·cm/cm | ASTM D256 | 1/8" bar |
23℃ (73℉) | *** kg·cm/cm | ASTM D256 | 1/8" bar |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | 23℃ |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 1/8" bar |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | All Color |
V-0 | *** mm | UL94 | All Color |
V-0 | *** mm | UL94 | All Color |
5VA | *** mm | UL94 | All Color |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.