Ultramid® 2710IR Bright is an unreinforced polyamide 66, impact modified, for injection moulding. This grade offers a good surface aspect and is used for fast cycle moulding.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Toughened/Impact ModifiedGood SurfaceFast Cycle Time | |||
| Additive | Impact Modifier | |||
| Appearance | Pellets/Granules | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Water Absorption | *** % | ISO 62 | 24 h in water, 23 °C |
Moisture /Humidity Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond. |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 2 in/min |
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Yield | *** Mpa | ISO 527-1/-2 | cond. |
Break | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | cond. |
Break | *** Mpa | ISO 527-1/-2 | cond. |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Yield | *** % | ISO 527-1/-2 | cond. |
Break | *** % | ASTM D638 | 2 in/min |
Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Modulus | *** Mpa | ISO 178 | cond. |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
- | *** Mpa | ISO 178 | cond. |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | cond. |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | cond. |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC (10°C/min) |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | cond. |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | cond. |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 62631-2-1 | |
100Hz | *** - | IEC 62631-2-1 | cond. |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Solution B | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | cond., d = 2.0 mm |
Dielectric Strength | *** kV/mm | IEC 60243-1 | d = 2.0 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.