25% Glass Reinforced, Flame Retardant, Non-Halogenated, Polybutylene Terephthalate
| Original Document | ||||
| Features | Flame RetardantHalogen FreeNon Red PhosphorusFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Appearance | Natural Color | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 2.00 mm, 50% RH |
Water Absorption | *** % | ISO 62 | Saturation, 23°C, 2.00 mm |
Bar flow | *** mm | - | 2.00 mm, 110 MPa |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | |
Poisson Ratio | *** - | - | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | 23 to 55°C |
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | -40 to 23°C |
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 55 to 160°C |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | -40 to 23°C |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | Pass |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.75mm | *** °C | IEC 60695-2-12 | |
1mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.75mm | *** °C | IEC 60695-2-13 | |
1.0mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
European Railways Certifications | *** HL | EN 45545-2 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
- | PLC | UL 746A | |
Dielectric Strength | *** kV/mm | IEC 60243-1 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.