Self-lubricating product based on Polyphenylene Sulphide (PPS).
PTFE. Carbon fibre.
| Original Document | Technical Datasheet(English) | |||
| Features | Self LubricatingFilled & Reinforced | |||
| Reinforced | 15% Carbon Fiber10% PTFE25% Carbon Fiber+PTFE | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | 2.0mm/60MPa |
Across Flow | ***~*** % | ISO 294-4 | 2.0mm/60MPa |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1 | 23°C, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1 | 23°C, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-1 | 23°C, 5 mm/min |
Coefficient of Friction | *** - | ASTM 1894 | dynamic |
Coefficient of Friction | *** - | ASTM 1894 | static |
Wear Factor | *** E-6 mm³/Nm | ASTM D 3702 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50 N (heating rate 50°C/h) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.