Ixef® BXT 2000-0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef® BXT 2000-0203 resin can be successfully extruded into tube, pipe, sheet and film and blow-molded into various profiles.
BXT 2000-0203 resin has proven permeation resistance to most automotive fluids and fuels. It also offers low moisture absorption, excellent dimensional stability, and chemical resistance as well as outstanding mechanical properties.
Natural: Ixef® BXT 2000-0203
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 尺寸稳定抗蠕变耐化学性耐燃油高流动低吸湿性高阻隔性 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出片材挤出型材挤出薄膜挤出管材挤出吹塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
- | 6 g/10min | Internal | 240℃ |
堆积(视)密度 | 0.7 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 63.4 Mpa | ASTM D638 | |
屈服(yld) | 63.8 Mpa | ISO 527-2 | |
断裂(brk) | 39.9 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 4 % | ASTM D638 | |
屈服(yld) | 3.7 % | ISO 527-2 | |
断裂(brk) | 44 % | ASTM D638 | |
标称断裂伸长率 | 77 % | ISO 527-2 | |
拉伸模量 | 2470 Mpa | ISO 527-1 | |
弹性模量 | 2480 Mpa | ASTM D 638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 350 J/m | ASTM D 256 | |
- | 15 kJ/m² | ISO 180 | |
悬臂梁无缺口(Izod Unnotched) | |||
- | 190 kJ/m² | ISO 180 | |
- | NB J/m | ASTM D 4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 82 °C | ISO 75-2/A | Unannealed |
熔融温度(Tm) | 230 °C | Internal | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
渗透性 | 0.83 g·mm/m²/atm/24 hr | SAE J2659 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。