Ixef® 3012 is a carbon-fiber and glass fiber reinforced polyarylamide compound which exhibits extremely high strength and stiffness, good surface gloss, excellent creep resistance, and lower density than glass-fiber reinforced engineering resins. Ixef® 3012 is also electrically conductive.
Black: Ixef® 3012 BK 001
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityElectrically ConductiveGood SurfaceDimensional StabilityCreep ResistantChemical ResistanceHigh FlowLow Moisture AbsorptionFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 55% Glass Fiber+Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | |
Across Flow | *** % | ASTM D955 | |
Moisture /Humidity Absorption | *** % | Internal | Saturation 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1 | |
Tensile Modulus | *** Mpa | ISO 527-1 | Conditioned |
Tensile Strength | |||
- | *** Mpa | ISO 527-2 | |
- | *** Mpa | ISO 527-2 | Conditioned |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | |
Break | *** % | ISO 527-2 | Conditioned |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
- | *** Mpa | ISO 178 | Conditioned |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Complete Break |
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Complete Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | Complete Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
Charpy Unnotched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Complete Break |
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Complete Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | Complete Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
Izod Notched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | |
Izod Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 0 to 80°C |
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 130 to 200°C |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 0 to 50°C |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 100 to 150°C |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | 150 to 200°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D 4496 | |
Surface Resistivity | *** Ohm | ASTM D 4496 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.