| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Mold Shrinkage | | | |
Flow |
***~*** % | ISO 294-4 | 2.0mm/60MPa |
Across Flow |
***~*** % | ISO 294-4 | 2.0mm/60MPa |
Moisture /Humidity Absorption |
*** %
| ISO 62-4 | in air, fter 24hrs |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ISO 527-1 | 120°C, 1 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527-1 | 150°C, 1 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527-1 | 23°C, 1 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527-1 | 60°C, 1 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527-1 | 90°C, 1 mm/min |
Tensile Strength | | | |
Yield |
*** Mpa | ISO 527-1 | 120°C, 5 mm/min |
Yield |
*** Mpa | ISO 527-1 | 150°C, 5 mm/min |
Yield |
*** Mpa | ISO 527-1 | 23°C, 5 mm/min |
Yield |
*** Mpa | ISO 527-1 | 60°C, 5 mm/min |
Yield |
*** Mpa | ISO 527-1 | 90°C, 5 mm/min |
Break |
*** Mpa | ISO 527-1 | 120°C, 5 mm/min |
Break |
*** Mpa | ISO 527-1 | 150°C, 5 mm/min |
Break |
*** Mpa | ISO 527-1 | 23°C, 5 mm/min |
Break |
*** Mpa | ISO 527-1 | 60°C, 5 mm/min |
Break |
*** Mpa | ISO 527-1 | 90°C, 5 mm/min |
Tensile Elongation | | | |
Yield |
*** % | ISO 527-1 | 120°C, 5 mm/min |
Yield |
*** % | ISO 527-1 | 150°C, 5 mm/min |
Yield |
*** % | ISO 527-1 | 23°C, 5 mm/min |
Yield |
*** % | ISO 527-1 | 60°C, 5 mm/min |
Yield |
*** % | ISO 527-1 | 90°C, 5 mm/min |
Break |
*** % | ISO 527-1 | 120°C, 5 mm/min |
Break |
*** % | ISO 527-1 | 150°C, 5 mm/min |
Break |
*** % | ISO 527-1 | 23°C, 5 mm/min |
Break |
*** % | ISO 527-1 | 60°C, 5 mm/min |
Break |
*** % | ISO 527-1 | 90°C, 5 mm/min |
Coefficient of Friction |
*** -
| ASTM 1894 | dynamic |
Coefficient of Friction |
*** -
| ASTM 1894 | static |
Wear Factor |
*** E-6 mm³/Nm
| ASTM D 3702 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75 | |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | 50 N (heating rate 50°C/h) |
Coefficient of Linear Thermal Expansion | | | |
Flow |
*** E-6/°C | ISO 11359-2 | 30 to 100°C |
Continuous Use Temperature | | | |
20000 hr |
*** °C | ASTM E1641 | |
20000 hr |
*** °C | ASTM E1877 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
V-1 |
*** mm | UL94 | |
V-0 |
*** mm | UL94 | |
V-0 |
*** mm | UL94 | |
Oxygen Index |
*** %
| ASTM D 2863 | |
Glow Wire Flammability Index(GWFI) | | | |
2mm |
*** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | | | |
1.0mm |
*** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity |
*** Ohm
| ASTM D257 | |
Comparative Tracking Index (CTI) | | | |
Solution A |
*** V | IEC 60112 | without surfactant |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.