Celazole® TKL-60 is a self-lubricating melt processable blend of PBI-PEKK (polyetherketoneketone).
Celazole® T-Series products are PBI compounds designed for injection molding and extrusion. Combining the superior mechanical properties and thermal resistance of PBI with the melt process ability of polyaryletherketones (PEEK or PEKK), these products offer cost-effective high performance. These products are available in pellet form.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 自润滑 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 注塑挤出 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.43 g/cm³ | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 125 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
- | 1 % | ASTM D 638 | |
弯曲强度 | |||
- | 180 Mpa | ASTM D790 | |
弯曲应变 | |||
- | 1.3 % | ASTM D 790 | |
弯曲模量 | 14600 Mpa | ASTM D790 | |
拉伸模量 | 17300 Mpa | ASTM D638 | |
摩擦系数 | 0.06 - | Internal | 50 fpm, PV 125K |
摩擦系数 | 0.08 - | Internal | 50 fpm, PV 50K |
摩擦系数 | 0.06 - | Internal | 800 fpm, PV 125K |
摩擦系数 | 0.06 - | Internal | 800 fpm, PV 250K |
摩擦系数 | 0.12 - | Internal | 800 fpm, PV 50K |
磨损因数 | 15 E-10 in3·min/ft·lb·hr | Internal | 50 fpm, PV 125K |
磨损因数 | 31 E-10 in3·min/ft·lb·hr | Internal | 50 fpm, PV 50K |
磨损因数 | 21 E-10 in3·min/ft·lb·hr | Internal | 800 fpm, PV 125K |
磨损因数 | 9 E-10 in3·min/ft·lb·hr | Internal | 800 fpm, PV 250K |
磨损因数 | 47 E-10 in3·min/ft·lb·hr | Internal | 800 fpm, PV 50K |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度E | 72 E | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 348 °C | DSC | |
玻璃化温度(Tg) | 171 °C | DSC | 1st |
玻璃化温度(Tg) | 425 °C | DSC | 2nd |
导热系数 | 0.5 W/(m K) | ASTM C518 | 100℃ |
导热系数 | 0.43 W/(m K) | ASTM C518 | 25℃ |