VALOX 4012G is a 10% glass fiber reinforced PBT injection molding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 短周期成型填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 10% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.39 g/cm³ | ISO 1183 | |
比重 | 1.39 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
250°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
250°C/1.2 kg | 10 g/10 min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.6~1.6 % | Internal | flow, 3.2 mm |
纵向(Flow) | 0.6~0.9 % | Internal | on Tensile Bar, flow |
横向(Across Flow) | 0.7~1 % | Internal | on Tensile Bar, xflow |
吸水率 | 0.2 % | ISO 62 | 23°C/sat |
吸湿率 | 0.07 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 75 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 72 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 72 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 75 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 4 % | ISO 527 | 5 mm/min |
断裂(brk) | 3 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 4 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 110 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 110 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 3940 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 4600 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 4500 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 7 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 45 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 45 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 74 J/m | ASTM D256 | |
-30℃ (-22℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 74 J/m | ASTM D256 | |
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 37 kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | 37 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 4 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 117 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 175 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 170 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 205 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 208 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 205 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 80 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 85 E-6/°C | ISO 11359-2 | 23°C to 150°C, xflow |
横向(Across Flow) | 80 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 750 °C | IEC 60695-2-12 | pass |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
介电常数(DK) | |||
50/60 Hz | 3.1 - | IEC 60250 | |
1MHz | 3 - | IEC 60250 | |
耗散因数(DF) | |||
50/60 Hz | 10 E-4 | IEC 60250 | |
1MHz | 14 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
溶液B | 150 V | IEC 60112 | M |
- | 250 V | IEC 60112 | |
绝缘强度 | 30 kV/mm | IEC 60243-1 | in oil, 0.8 mm |
绝缘强度 | 25 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
绝缘强度 | 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。