| Original Document | Technical Datasheet(English) | |||
| Features | High Barrier property/Low permeation | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
210℃/2.16kg | *** g/10 min | ISO 1133 | |
Ethylene Content | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | |
Tensile Elongation | |||
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | |
Melt Temperature(Tm) | *** °C | ISO 11357 | |
Glass Transition Temperature | *** °C | ISO 11357 | |
Freezing temperature | *** °C | ISO 11357 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Water Vapor Transmission Rate | *** g.mm/m².24hr | ASTM E96 | |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 0%RH, 20°C |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 100%RH, 20°C |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 35%RH, 20°C |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 65%RH, 20°C |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 85%RH, 20°C |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ISO 14663-2 | 90%RH, 20°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.