VALOX 310SE0 is an unreinforced, flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.71mm and 5VA@3.0mm flame rating.
This is a good candidate for thin wall applications in the electrical industry including bobbins,keyboards, switches and appliance housings.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃耐化学性 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
比重 | 1.4 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
250℃/2.16 kg | 8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
250°C/2.16 kg | 8.6 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.9~1.6 % | Internal | flow, 0.75-2.3 mm |
纵向(Flow) | 1.5~2.3 % | Internal | flow, 2.3-4.6 mm |
纵向(Flow) | 1.5~2.3 % | Internal | flow, 3.2 mm |
纵向(Flow) | 1.1~1.8 % | Internal | on Tensile Bar, flow |
横向(Across Flow) | 0.9~1.9 % | Internal | on Tensile Bar, xflow |
横向(Across Flow) | 1~1.7 % | Internal | xflow, 0.75-2.3 mm |
横向(Across Flow) | 1.6~2.4 % | Internal | xflow, 2.3-4.6 mm |
吸水率 | 0.36 % | ISO 62 | 23°C/sat |
吸湿率 | 0.08 % | ISO 62 | 23°C / 50% RH |
比容 | 0.71 cm³/g | ASTM D792 | |
磨耗 | 19 mg/1000cy | Internal | CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 58 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 40 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
断裂(brk) | 18 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 18 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 101 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 90 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2620 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2600 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2820 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2800 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 5 kJ/m² | ISO 179/2C | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 25 J/m | ASTM D256 | |
-30℃ (-22℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 40 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 200 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 120 R | ISO 2039-2 | |
球压硬度 | 105 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 162 °C | ASTM D648 | 6.4 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 150 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 74 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 71 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 73 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 60 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 170 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 212 °C | ISO 306 | Rate A/50 |
维卡软化温度(Vicat) | 170 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 170 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 120 °C | UL 746B | |
电气Elec,- | 120 °C | UL 746B | |
强度Str,- | 140 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 79.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 131 E-6/°C | ASTM E831 | 60°C to 138°C, flow |
纵向(Flow) | 76 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
纵向(Flow) | 100 E-6/°C | ISO 11359-2 | 23°C to 60°C, flow |
横向(Across Flow) | 79.2 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 73 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
横向(Across Flow) | 100 E-6/°C | ISO 11359-2 | 23°C to 60°C, xflow |
导热系数 | 0.24 W/m-°C | ISO 8302 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.71 mm | UL94 | |
5VA | 3 mm | UL94 | |
氧指数(LOI) | 30 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | ROA |
介电常数(DK) | |||
50/60 Hz | 2.9 - | IEC 60250 | |
100Hz | 3.1 - | IEC 60250 | |
1MHz | 2.8 - | IEC 60250 | |
耗散因数(DF) | |||
50/60 Hz | 10 E-4 | IEC 60250 | |
100Hz | 20 E-4 | IEC 60250 | |
1MHz | 125 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
溶液B | 100 V | IEC 60112 | M |
- | 175 V | IEC 60112 | |
- | 3 PLC | UL 746A | |
绝缘强度 | 18.4 kV/mm | ASTM D149 | in air, 3.2 mm |
绝缘强度 | 24 kV/mm | ASTM D149 | in oil, 1.6 mm |
绝缘强度 | 35 kV/mm | IEC 60243-1 | in oil, 0.8 mm |
绝缘强度 | 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
绝缘强度 | 25 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
绝缘强度 | 18 kV/mm | IEC 60243-1 | shorttime, 1.0mm |
耐电弧性 | 6 PLC | UL 746A | Tungsten |
高电压电弧起痕速率(HVTR) | 4 PLC | UL 746A | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | |
高压低流耐电弧性(HVAR) | 6 PLC | UL 746A |