PC/ABS Blend general purpose grade high flow
| Original Document | Technical Datasheet(English) | |||
| Features | High Flow | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
260°C/5.0 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | Linear Mould Shrinkage |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | |
Break | *** Mpa | ISO 527 | |
Tensile Elongation | |||
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Ball Pressure Test | *** °C | IEC 60335-1 | Pass |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | |
Burning Rate | *** mm/min | ISO 3795 | FMVSS 302 |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Oil 1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.