PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Lubricated, Black Color
Specification Approvals
MS.50017 (MS-DB-41) CPN 1900, WSS-M4D673-B1
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedLubricatedFilled & Reinforced | |||
| Additive | Heat StabilizerLubricant | |||
| Appearance | Black | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | 1/8 in. |
Water Absorption | *** % | ISO 62 | 24 hr. Immersed |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1 | Conditioned 50% RH |
Break | *** Mpa | ISO 527-1 | Dry |
Tensile Elongation | |||
Break | *** % | ISO 527-1 | Conditioned 50% RH |
Break | *** % | ISO 527-1 | Dry |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned 50% RH |
Flexural Modulus | *** Mpa | ISO 178 | Dry |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned 50% RH |
- | *** Mpa | ISO 178 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned 50% RH |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned 50% RH |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.