INVISTA U4840NL NC01 is a highly nucleated PA66 resin designed for injection molding where fast crystallization and fast cycle times are required. It is lubricated internally and externally for excellent machine feed and mold release.
Features
• Very fast crystallization
• Excellent processability
• Excellent whiteness
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 润滑的易成型短周期成型易脱模 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.4 % | ISO 294-4 | 2.0 mm |
横向(Across Flow) | 1.5 % | ISO 294-4 | 2.0 mm |
吸水率 | 1.4 % | ISO 62 | 24 hours |
吸水率 | 2.6 % | ISO 62 | equilibrium @ 50% RH |
粘度 | 137 cm³/g | ISO 307 | VN at 0.5% in formic acid, nominal |
粘度 | 150 cm³/g | ISO 307 | VN at 0.5% in sulfuric acid, nominal |
粘度 | 2.7 - | Internal | RV at 1% in sulfuric acid, nominal |
粘度 | 48 - | ASTM D 789 | RV in formic acid, nominal |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 93 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 4 % | ISO 527 | |
断裂(brk) | 15 % | ISO 527 | |
弯曲强度 | |||
- | 99 Mpa | ISO 178 | |
弯曲模量 | 3100 Mpa | ISO 178 | |
拉伸模量 | 3700 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3.1 kJ/m² | ISO 179 | |
23℃ (73℉) | 3.7 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179 | |
23℃ (73℉) | NB kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 4.7 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 230 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 80 °C | ISO 75 | |
熔融温度(Tm) | 263 °C | ISO 11357 | 10°C/min |
球压痕温度 | 240 °C | IEC 60695-10-2 | 3.0 mm |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.4 mm | UL94 | |
V-2 | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.71mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | 3.0 mm |
绝缘强度 | 18 kV/mm | IEC 60243 | 1.0 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746A | |
高压低流耐电弧性(HVAR) | 5 PLC | UL 746A |