INVISTA U4820L NC01 is a general purpose natural PA66 resin suitable for injection molding and extrusion applications where fast cycles are required. It is lubricated internally and externally for excellent machine feed and mold release.
Features
Excellent whiteness and processability
Classification
ASTM D4066 classification PA0111
| Original Document | Technical Datasheet(English) | |||
| Features | LubricatedEasy processingFast Cycle TimeMold Release | |||
| Processing | InjectionExtrusion | |||
| Compliance | RoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 2.0 mm |
Across Flow | *** % | ISO 294-4 | 2.0 mm |
Water Absorption | *** % | ISO 62 | 24 hours |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | equilibrium @ 50% RH |
Viscosity | *** cm³/g | ISO 307 | VN at 0.5% in formic acid, nominal |
Viscosity | *** cm³/g | ISO 307 | VN at 0.5% in sulfuric acid, nominal |
Viscosity | *** - | Internal | RV at 1% in sulfuric acid, nominal |
Viscosity | *** - | ASTM D 789 | RV in formic acid, nominal |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Modulus | *** Mpa | ISO 527 | 50% RH |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | |
Yield | *** Mpa | ISO 527 | 50% RH |
Tensile Elongation | |||
Yield | *** % | ISO 527 | |
Yield | *** % | ISO 527 | 50% RH |
Break | *** % | ISO 527 | |
Break | *** % | ISO 527 | 50% RH |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Modulus | *** Mpa | ISO 178 | 50% RH |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
- | *** Mpa | ISO 178 | 50% RH |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | 50% RH |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | 50% RH |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | 50% RH |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | 50% RH |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | |
23℃ (73℉) | *** kJ/m² | ISO 180 | 50% RH |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359 | 23 - 55 °C |
Across Flow | *** E-6/°C | ISO 11359 | 23 - 55 °C |
Melt Temperature(Tm) | *** °C | ISO 11357 | 10°C/min |
Ball Pressure Test | *** °C | IEC 60695-10-2 | 3.0 mm |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | 50% RH |
V-2 | *** mm | UL94 | 50% RH |
V-2 | *** mm | UL94 | 50% RH |
V-2 | *** mm | UL94 | 50% RH |
Glow Wire Flammability Index(GWFI) | |||
0.71mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | 2.0 mm |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | 3.0 mm |
Dielectric Strength | *** kV/mm | IEC 60243 | 1.0 mm |
High Voltage Arc Tracking Rate(HVTR) | PLC | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.