This high density polyethylene is an ethylene-hexene copolymer tailored for injection molding applications that require:
• Excellent stiffness
• Good impact strength
• Durability
• Moderate flow
Typical injection molding applications for HMN 6060 include:
• Crates • Tote boxes
• Structural foam (with proper foaming agent)
This resin meets these specifications:
• ASTM D4976 – PE 233
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c)
| Original Document | Technical Datasheet(English) | |||
| Features | Good StiffnessDurabilityGood Impact ResistanceFoamableGood Flow | |||
| Processing | InjectionFoam | |||
| Compliance | ASTM D4976FDA | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
Environmental Stress Cracking Resistance | *** Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Tangent - 16:1 span:depth, 0.5 in/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 2 in/min, Type IV bar/min |
Break | *** % | ASTM D638 | 2 in/min, Type IV bar |
Flexural Modulus | *** Mpa | ASTM D790 | 1 % Secant, 16:1 span:depth, 0.5 in/min |
Flexural Modulus | *** Mpa | ASTM D790 | Tangent, 16:1 span:depth, 0.5 in/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Instrumented Impact Energy | |||
23℃ (73℉)peak | *** J | ASTM D3763 | 21.6 ft/sec, 73.4 °F, 0.125 in |
23℃ (73℉)Total Energy | *** J | ASTM D3763 | 21.6 ft/sec, 73.4 °F, 0.125 in |
Brittleness Temperature | *** °F | ASTM D 746 | Type A, Type I specimen |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Method A |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Method A |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Loading 1, Rate A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.