This extra high molecular weight, ethylene-hexene copolymer is tailored for large blow molded and thermoformed parts that require:
• Good melt strength
• Good rigidity
• Exceptional ESCR
• Excellent low temperature impact strength
• Durability
Typical blow molded applications for HXM 50100 include:
• Shipping containers • Jerry cans • Fuel containers • Agricultural chemical tanks
Typical thermoformed applications for HXM 50100 include:
• Pallets • Automotive dunnage • Truck bedliners • Playground equipment
This resin meets these specifications:
• ASTM D4976 - PE 235
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c)
• UL94HB yellow card per UL file E349283
• NSF Standard 61 for potable water
• Listed in the Drug Master File
| Original Document | Technical Datasheet(English) | |||
| Features | DurabilityHigh Impact at Low TemperaturFood ContactDrinking Water ContactESCRHigh melt strength | |||
| Processing | Blow MoldingThermoforming | |||
| Compliance | ASTM D4976Drug Master FileFDANSF | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
Environmental Stress Cracking Resistance | *** Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 2 in/min, Type IV bar |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 2 in/min, Type IV bar |
Flexural Modulus | *** Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Impact | *** kJ/m² | ASTM D 1822 | Type S bar |
Brittleness Temperature | *** °C | ASTM D 746 | Type A, Type I specimen |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Method A |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Loading 1, Rate A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.