K8003 is a polypropylene impact copolymer with excellent stiffness and ultrahigh impact performance, which is widely used in area of injection molding, extrusion molding and blending modification.
Typical Applications
Injection Molding: lubricating oil drum, storage battery case, power tool parts, baby carrier parts, toys, plastic tray
Extrusion Molding: sheets, non-compression-bearing pipes
Blending Modification: automobile parts, household appliance parts
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High ImpactCopolymer | |||
| Processing | InjectionExtrusionSheet ExtrusionTube ExtrusionCompounding | |||
| Compliance | FDAGB 4806.6-2016RoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | GB/T 1033 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | GB/T 3682 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | GB/T 1040.2 | 50 mm/min |
Break | *** Mpa | GB/T 1040.2 | 50 mm/min |
Tensile Elongation | |||
Break | *** % | GB/T 1040.2 | 50 mm/min |
Flexural Modulus | *** Mpa | GB/T 9341 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | GB/T 1043.1 | |
23℃ (73℉) | *** kJ/m² | GB/T 1043.1 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | GB/T 3398.2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | GB/T 1634.2 | |
Vicat Softening Temperature(VST) | *** °C | GB/T 1633 | A50 |
Melt Temperature(Tm) | *** °C | GB/T 19466.3 | DSC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.