3M™ Dyneon™ Fluoroelastomer FT 2320 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The “dry” ingredients should be blended before adding to the masticated gum. For best results, Dyneon FT 2320 should be banded on the mill several minutes prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stability
Features and Benefits
• Composition: terpolymer of vinylidene fluoride, hexafluoropropylene, and tetrafluoroethylene • Low viscosity • Process targets: injection extrusion and calendering • Proprietary incorporated cure technology
| Original Document | Technical Datasheet(English) | |||
| Features | Low viscosity | |||
| Processing | CalenderingInjectionExtrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | |
Mooney Viscosity | *** MU | Internal | ML 1 + 10 @ 121°C |
Fluorine Content | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | Internal | |
at 100% strain | *** Mpa | Internal | |
Tensile Elongation | |||
Break | *** % | Internal | |
Compression Set | *** % | ASTM D 395 | 200°C, 70 hr |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Low Temp. Retraction | *** °C | ASTM D1329 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.