Polyimide Isostatic Shapes
DuPont™ Vespel® SCP-50094 is a proprietary polymer. It is designed for demanding applications that require high temperature and wear resistance.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat ResistanceWear/Abrasion Resistance | |||
| Appearance | Parts/ Shapes | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23 °C |
Water Absorption | *** % | ASTM D570 | 23 °C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | 23 °C |
- | *** Mpa | ASTM D 638 | 260 °C |
Tensile Elongation | |||
- | *** % | ASTM D 638 | 23 °C |
- | *** % | ASTM D 638 | 260 °C |
Flexural Modulus | *** Mpa | ASTM D790 | 23 °C |
Flexural Modulus | *** Mpa | ASTM D790 | 260 °C |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 23 °C |
- | *** Mpa | ASTM D790 | 260 °C |
Poisson Ratio | *** - | ASTM D 638 | 23 °C |
Poisson Ratio | *** - | ASTM D 638 | 260 °C |
Coefficient of Friction | *** - | Internal | 0.88 (25K) PV, 0.7 m/s (134 fpm), 1.3 MPa (187 psi) |
Coefficient of Friction | *** - | Internal | 10.50 (300K) PV, 3.0 m/s (585 fpm), 3.5 MPa (500 psi) |
Coefficient of Friction | *** - | Internal | 3.50 (100K) PV, 2.0 m/s (400 fpm), 1.7 MPa (250 psi) |
Wear Factor | *** E-10 in3·min/ft·lb·hr | Internal | 0.88 (25K) PV, 0.7 m/s (134 fpm), 1.3 MPa (187 psi) |
Wear Factor | *** E-10 in3·min/ft·lb·hr | Internal | 10.50 (300K) PV, 3.0 m/s (585 fpm), 3.5 MPa (500 psi) |
Wear Factor | *** E-10 in3·min/ft·lb·hr | Internal | 3.50 (100K) PV, 2.0 m/s (400 fpm), 1.7 MPa (250 psi) |
Modulus of Elasticity | *** Mpa | ASTM D 638 | 23 °C |
Modulus of Elasticity | *** Mpa | ASTM D 638 | 260 °C |
Compressive Strength | *** Mpa | ASTM D 695 | 23 °C |
Compressive Strength | *** Mpa | ASTM D 695 | 23 °C, 10% Strain |
Compressive Strength | *** Mpa | ASTM D 695 | 260 °C |
Compressive Strength | *** Mpa | ASTM D 695 | 260 °C, 10% Strain |
Compressive Creep | *** % | ASTM D2990 | 10 hr, 23 °C, 10 MPa |
Compressive Creep | *** % | ASTM D2990 | 10 hr, 23 °C, 14 MPa |
Compressive Creep | *** % | ASTM D2990 | 100 hr, 23 °C, 10 MPa |
Compressive Creep | *** % | ASTM D2990 | 100 hr, 23 °C, 14 MPa |
Compressive Creep | *** % | ASTM D2990 | 1000 hr, 23 °C, 10 MPa |
Compressive Creep | *** % | ASTM D2990 | 1000 hr, 23 °C, 14 MPa |
Compressive Strain | *** % | ASTM D695 | 23 °C |
Compressive Strain | *** % | ASTM D695 | 260 °C |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell E | *** E | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Specific Heat | *** J/kg/°C | ASTM E 1269 | 60 °C |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 m/m/℃ | ASTM E831 | 50–150 °C |
Across Flow | *** E-6 m/m/℃ | ASTM E831 | 50–150 °C |
Thermal Conductivity | *** W/(m K) | ASTM F433 | 100 °C |
Thermal Conductivity | *** W/(m K) | ASTM F433 | 300 °C |
Thermal Conductivity | *** W/(m K) | ASTM F433 | 50 °C |
Deformation | *** % | ASTM D621 | 23 °C, 14 MPa, 24 hours |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.