SABIC PP PHC31-81 is a grade which combines high stiffness with good impact strength. Its excellent flow properties and narrow molecular weight distribution permits fast cycle-times and injection moulding of articles demanding low warpage and high dimensional stability.
This grade is formulated with a combined processing and UV-stabilisation package.
Typical applications are automotive components. It is also available in a general purpose additive package.
SABIC PP PHC31-81 is a designated automotive grade.
IMDS ID: 80775790
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityGood Impact ResistanceDimensional StabilityLow WarpageFast Cycle TimeUV StabiltiyCopolymer | |||
| Additive | UV-StabilizerProcessing Aid | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | Internal | 24 hours after injection moulding |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
0℃ (32℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
0℃ (32℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 80*10*4mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 80*10*4mm |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B | 120°C/h, at 50 N (VST/B) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A | 120°C/h, at 10 N (VST/A) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.