SABIC PP 95610 is a reactor-elastomer-modified material which offers an excellent cold impact resistance.
It is a highly attractive alternative to non-filled compounds and is commonly used for car bumpers.
SABIC PP 95610 is a designated automotive grade.
IMDS ID: 80775790
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHigh Impact at Low Temperatur | |||
| Reinforced | Elastomer | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | Internal | 24 hours after injection moulding |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 179/1eA | |
0℃ (32℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
0℃ (32℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B | 120°C/h, at 50 N (VST/B) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A | 120°C/h, at 10 N (VST/A) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.