SABIC PP 500P is a medium flow, multipurpose grade for extrusion and injection molding applications.
TYPICAL APPLICATIONS
If applied for extrusion 500P shows an excellent stretch ability and is therefore suitable for tapes and strapping, high tenacity yarns and carpet backing. It can also be used in ropes and twines, woven bags, flexible intermediate bulk containers, geotextiles and concrete reinforcements.
For thermoforming it shows a unique balance between transparency, impact resistance and thickness uniformity.
500P is also suitable for production of injection molded articles e.g. caps and closures and house ware products, where this grade shows a high stiffness, combined with a fair impact resistance and very good surface hardness.
| Original Document | Technical Datasheet(English) | |||
| Features | Medium viscosityHomopolymer | |||
| Processing | InjectionExtrusionSpinning/MonofilamentThermoforming | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 80*10*4mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 80*10*4mm |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B | 120°C/h, at 50 N (VST/B) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A | 120°C/h, at 10 N (VST/A) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.