Modified Polypropylene
FEATURES:
- High Stiffness and Good Impact Strength
- High Heat Resistance
- Low Shrinkage and Low Warpag
- Color According to Customer Requirement
APPLICATIONS:
- Injection molding
- Industrial Bobbin’s
- Propeller Fan
- Automobile Intercooler Cover
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityGood Impact ResistanceHeat ResistanceLow WarpageLow Shrinkage | |||
| Appearance | Pellets/GranulesColors Available | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23℃ |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ISO 294 | 23℃ |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ISO 527 | 50mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | 50mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | 4mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.