Glass Fiber Reinforced PBT
FEATURES:
- Good toughness
- High heat resistance
- Good dimensional stability
APPLICATIONS:
- Connectors
- Auto’s parts
- Other E&E parts
| Original Document | Technical Datasheet(English) | |||
| Features | Good ToughnessHeat ResistanceDimensional StabilityFilled & Reinforced | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 2577 | |
Across Flow | *** % | ISO 2577 | |
Water Absorption | *** % | ISO 62 | Equilibrium 23℃/50% r.h. |
Filled/Ash | *** % | ISO 3451 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527-2 | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 2mm, in oil |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.