Delrin® SC698 NC010 is a lubricated low viscosity acetal homopolymer, developed for high precision thin-walled parts requiring low wear and low friction with excellent surface aspect.
SPECIAL CONTROL for HEALTHCARE APPLICATIONS
This product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. This product is also tested against ISO 10993-5 and -11 and selected parts of USP Class VI. For details, individual compliance statements are available from your DuPont representative.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好表面耐磨低摩擦润滑的尺寸稳定食品接触级医疗级低粘度均聚物 | |||
| 添加助剂 | 脱模剂润滑剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | FDA(食品药品监督管理局)ISO10993(生物相容性) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.44 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 23 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.6 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
熔体密度 | 1.14 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 65 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 11 % | ISO 527-1/-2 | |
标称断裂伸长率 | 14 % | ISO 527-1/-2 | |
拉伸模量 | 3100 Mpa | ISO 527-1/-2 | |
泊松比 | 0.37 - | - | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 85 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 90 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
比热容 | 3020 J/kg-K | - | melt |
熔融温度(Tm) | 178 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.22 W/(m K) | - | melt |
加工温度 | 210~220 °C | - | |
模具温度 | 80~100 °C | - |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。