with PTFE, lubricant modified, dark grey
Main features:
Improved friction and wear behaviour. Optimised for dry running operations. Chemically- and hydrolytically- resistant parts, non flammable. High dimensionally stable precision parts.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Flame RetardantWear/Abrasion ResistanceLow Friction/WearLubricatedDimensional StabilityChemical ResistanceHydrolysis Resistance | |||
| Appearance | Pellets/GranulesGray Color | |||
| Reinforced | PTFE | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
380°C/10 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | DIN 16742 | |
Water Absorption | *** % | ISO 62 | 23°C / 24h |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | dry, @1 mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527 | dry, @50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | dry, @50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | dry, @2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | dry, @10 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | dry, 80x10x4mm |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | dry, 80x10x4mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A | |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
Temperature at Short Circle Operation | *** °C | IEC 60216 | during lifetime max. 200h |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Insulation Resistance | *** Ohm | IEC 60167 | R25 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.