with carbon fibers, heat stabilized, natural color (black)
Main features:
Very strong and stiff parts; low coefficient of thermal expansion. Reduced moment of inertia compared with metal parts. Electrically conductive, suitable for continuous discharging of statically-generated electricity. High dimensionally stable precision parts with low warpage and narrow tolerance range.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceHeat StabilizedElectrically ConductiveAnti-StaticDimensional StabilityLow WarpageLow CLTEFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Reinforced | 40% Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294 | 60x60x2 mm |
Across Flow | *** % | ISO 294 | 60x60x2 mm |
Water Absorption | *** % | ISO 62 | 23°C / 24h |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | dry, @1 mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527 | dry, @50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | dry, @50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | dry, @2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | dry, @10 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | dry, @10 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | 80x10x4mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | dry, 80x10x4mm |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1fU | 80x10x4mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1fU | dry, 80x10x4mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359 | 10x8x4 mm |
Thermal Conductivity | *** W/(m K) | ISO 22007 | in plane, hot disk |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
Temperature at Short Circle Operation | *** °C | IEC 60216 | during lifetime max. 200h |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | IEC 60093 | ROB |
Insulation Resistance | *** Ohm | IEC 60167 | R25 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.