TECAPEEK SE natural - Stock Shapes (rods, plates, tubes)
Main features
- good heat deflection temperature; good machinability; inherent flame retardant resistance; against high energy radiation; good slide and wear properties; very good chemical resistance; high creep resistance; hydrolysis and superheated steam resistant
Target Industries
-semiconductor technology
| Original Document | Technical Datasheet(English) | |||
| Features | Heat ResistanceFlame RetardantWear/Abrasion ResistanceLow Friction/WearCreep ResistantGamma ResistanceSteam ResistantChemical ResistanceHydrolysis Resistance | |||
| Appearance | SheetRodpipeOpaque ColorBeige | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | |
Water Absorption | *** % | ISO 62 | 24h, 23°C |
Water Absorption | *** % | ISO 62 | 96h, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | 50mm/min |
- | *** Mpa | ISO 527-2 | 50mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | 50mm/min |
Break | *** % | ISO 527-2 | 50mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2mm/min, 10 N |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2mm/min, 10 N |
Compressive Modulus | *** Mpa | ISO 604 | 5mm/min, 10 N |
Compressive Strength | *** Mpa | ISO 604 | 1%, 5mm/min, 10 N |
Compressive Strength | *** Mpa | ISO 604 | 2%, 5mm/min, 10 N |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
- | *** kJ/m² | ISO 179/1eA | max. 7,5J |
Charpy Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 179/1eU | max. 7,5J |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Specific Heat | *** J/g-°C | ISO 22007-4 | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359-1/-2 | 100-150°C, long. |
- | *** E-6/K | ISO 11359-1/-2 | 23-100°C, long. |
- | *** E-6/K | ISO 11359-1/-2 | 23-60°C, long. |
Melt Temperature(Tm) | *** °C | ISO 11357 | |
Glass Transition Temperature | *** °C | ISO 11357 | |
Thermal Conductivity | *** W/(m K) | ISO 22007-4 | |
Continuous Use Temperature | |||
Long term | *** °C | Internal | long term |
Temperature at Short Circle Operation | *** °C | Internal | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | IEC 60695-11-10 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Silver electrode, 23°C, 12% r.h. |
Surface Resistivity | *** Ohm | IEC 60093 | Silver electrode, 23°C, 12% r.h. |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | Platin electrode, 23°C, 50% r.h. |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 23°C, 50% r.h. |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.