Description
J-370A is high impact block copolymer which has high ethylene-propylene rubber content. This grade is designed to be processed in Injection molding equipments by improvement in mold release and anti-static.
J-370A show high melt flow, low blush and has good balance of strength, impact resistance.
Applications
- home appliances case & cover, humidity-absorption container
- Base resin for compounding
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactMold ReleaseFood ContactHigh Flow | |||
| Additive | Antistatic Additive | |||
| Compliance | FDA | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Yield | *** Mpa | ISO 527-1 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Break | *** % | ISO 527-1 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-10℃ (14℉) | *** J/m | ASTM D256 | |
-10℃ (14℉) | *** J/m | ISO 180 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.