Description
J-370A is high impact block copolymer which has high ethylene-propylene rubber content. This grade is designed to be processed in Injection molding equipments by improvement in mold release and anti-static.
J-370A show high melt flow, low blush and has good balance of strength, impact resistance.
Applications
- home appliances case & cover, humidity-absorption container
- Base resin for compounding
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击易脱模食品接触级高流动 | |||
| 添加助剂 | 抗静电剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ISO 1183 | |
密度 | 0.9 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 35 g/10min | ASTM D 1238 | |
230°C/2.16 kg | 35 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 26 Mpa | ASTM D638 | |
屈服(yld) | 25 Mpa | ISO 527-1 | |
拉伸延伸率 | |||
断裂(brk) | 50 % | ASTM D638 | |
断裂(brk) | 100 % | ISO 527-1 | |
弯曲模量 | 1470 Mpa | ASTM D790 | |
弯曲模量 | 1270 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-10℃ (14℉) | 29 J/m | ASTM D256 | |
-10℃ (14℉) | 25 J/m | ISO 180 | |
23℃ (73℉) | 58 J/m | ASTM D256 | |
23℃ (73℉) | 54 J/m | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 125 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 105 °C | ISO 75-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。