ExxonMobil™ LL 1002xBU resin is an ethylene 1-butene linear low density polyethylene designed for the blown film process. It offers high gloss and excellent draw down. Films made from LL 1002xBU have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002xBU resin.
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂增滑剂开口剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 流延薄膜成型灌装封口(FFS)薄膜挤出吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 94 °C | Internal | |
熔融温度(Tm) | 123 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 23 % | ASTM D1003 | |
光泽度 | 28 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 8.7 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.8 Mpa | ASTM D 882 | TD |
断裂(brk) | 36 Mpa | ASTM D 882 | MD |
断裂(brk) | 27 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 620 % | ASTM D 882 | MD |
断裂(brk) | 770 % | ASTM D 882 | TD |
穿透强度 | 21 N | Internal | |
耐穿透性 | 0.8 J | Internal | |
埃尔曼多夫撕裂 | 110 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 390 g | ASTM D 1922 | TD |
割线模量 | 170 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 210 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 60 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。