A high crystallinity, medium impact copolymer resin with high melt flow rate and excellent processing attributes. It is designed for injection molded large appliance applications and automotive interior parts.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High Stiffness/RigidityMedium Impact ResistanceEasy processingFast Cycle TimeHigh Flow | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 51 mm/min |
Yield | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 51 mm/min |
Yield | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 1.3 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 13 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
-20℃ (-4℉) | *** kJ/m² | ISO 179/1eA | |
0℃ (32℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | |
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
-18℃ (0℉) | *** J/m | ASTM D 256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Falling Dart Impact | *** J | ASTM D 5420 | Gardner Impact (-29°C, 3.18 mm) |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.